7Cr7Mo3V2Si钢适宜制造承受高负荷的冷挤、冷镦、冷冲模具
|
C |
Cr |
Mo |
V |
Si |
Mn |
P |
S |
|
0.70~0.80 |
6.50~7.50 |
2.00~3.0 |
1.70~2.20 |
0.70~1.20 |
≤0.50 |
≤0.030 |
≤0.030 |
7Cr7Mo3V2Si钢的热加工条件
|
加热温度/℃ |
始锻温度/℃ |
终锻温度/℃ |
冷 却 |
|
1120~1130 |
1100 |
≥850 |
缓冷（坑冷或砂冷） |